Chitin nanowhisker composites and methods

ABSTRACT

A composite includes particles of thermoplastic polymer coated with a chitin nanowhisker gel and melt-blended. The thermoplastic polymer may be polystyrene, polyethylene, acrylonitrile butadiene styrene, polycarbonate, or another thermoplastic polymer.

CROSS-REFERENCE TO RELATED APPLICATION

This application is filed under 35 U.S.C. 121 as a divisional of U.S. patent application Ser. No. 13/935,621 filed on Jul. 5, 2013, the contents of which are incorporated herein by reference.

FIELD OF THE INVENTION

The following relates generally to nanocomposites and more particularly to chitin nanowhisker composites, methods of fabricating chitin nanowhisker composites, and methods of processing chitin.

BACKGROUND OF THE INVENTION

Nanoparticles are particles having one or more dimensions between 1 and 100 nanometers (nm). Due primarily to a high percentage of their atoms being positioned at the surface providing a very large surface area for their size, nanoparticles of a given material can exhibit markedly different properties and behaviours than larger particles of the same material.

Nanocomposites are multiple-phase materials, found in nature or fabricated, where one of the phases is nanoparticles. For example, a solid nanocomposite comprises nanoparticles dispersed in a bulk solid matrix. Due to the unique physical properties of nanoparticles, a small percentage of nanoparticles can have noticeable, macro-scale effects on the bulk solid matrix. As such, fabrication of nanocomposites having nanoparticles for imparting beneficial macro-scale mechanical, electrical, optical, dielectrical, thermal, antimicrobial or other effects is of great interest.

Nanofibrils, or nanowhiskers, are nanoparticles having a crystalline rod-like structure. Chitin nanowhiskers include crystalline polysaccharides having a diameter of about 10 nm and a length of about 200 nm to about 500 nm that may be found in an abundant, biodegradable and non-toxic structural polysaccharide material found in crustaceans such as shrimp and crab, known as chitin. Chitin nanowhiskers are desirable for nanocomposites due to their ability to impart desirable mechanical and antimicrobial effects, as well as due to their biodegradability, their abundance and their non-toxicity.

In nature, chitin contains both amorphous and crystalline chitin along with various other components such as proteins and the like. For forming nanocomposites, it is desirable to extract mostly individual chitin nanowhiskers from chitin so that the individual nanowhiskers can be dispersed throughout a bulk matrix. As such, it is desirable to process the chitin to generally extract only individual chitin nanowhiskers, without also extracting agglomerated chitin nanowhiskers that can be undesirably larger in size, amorphous chitin, and the proteins or other materials.

When forming the nanocomposites on an industrial scale using chitin nanowhiskers, it can be challenging to ensure that nanoparticles are generally uniformly dispersed in the bulk solid matrix. Unless the chitin nanowhiskers are dispersed in this way, an overall body of nanocomposite material will not exhibit the desirable properties uniformly. Too low a concentration of chitin nanowhiskers will have little beneficial effect, while too high a concentration of chitin nanowhiskers can undesirably weaken the material locally. Furthermore, if the overall body of nanocomposite material is to be subdivided into pellets or other smaller units prior to provision to a downstream process, there can be a wide variation in amounts of chitin nanowhiskers across individual pellets.

SUMMARY OF THE INVENTION

According to an aspect, there is provided a composite comprising particles of thermoplastic polymer coated with a chitin nanowhisker gel and melt-blended.

In an embodiment, the thermoplastic polymer comprises polypropylene. In another embodiment, the thermoplastic polymer comprises polyethylene. In another embodiment, the thermoplastic polymer comprises acrylonitrile butadiene styrene. In another embodiment, the thermoplastic polymer comprises polycarbonate. In another embodiment, the composite comprises various thermoplastic polymers.

According to another aspect, there is provided a composite comprising chitin nanowhiskers dispersed in polypropylene.

According to another aspect, there is provided a composite comprising chitin nanowhiskers dispersed in polyethylene.

According to another aspect, there is provided a composite comprising chitin nanowhiskers dispersed in acrylonitrile butadiene styrene.

According to another aspect, there is provided a composite comprising chitin nanowhiskers dispersed in polycarbonate.

Other aspects may become apparent to the ordinary skilled reader upon review of the following.

BRIEF DESCRIPTION OF THE DRAWINGS

Embodiments of the invention will now be described with reference to the appended drawings in which:

FIG. 1 is a flowchart showing steps in a method for processing chitin;

FIG. 2 is an image captured, using an atomic force microscope (AFM) using peak force error mode, of chitin nanowhiskers, wherein the scale bar is included within the image;

FIG. 3 is an image captured, using a transmission electron microscope (TEM), of chitin nanowhiskers;

FIG. 4 is another image captured, using a TEM, of chitin nanowhiskers;

FIG. 5 is another image captured, using a TEM, of chitin nanowhiskers;

FIG. 6 is a flowchart showing steps in a method of forming a composite including chitin nanowhiskers dispersed in a thermoplastic polymer matrix;

FIG. 7 is a graph showing a stress/strain curve for polypropylene (PP) and a counterpart PP-chitin nanowhisker composite (PP nC);

FIG. 8 is a graph showing a stress/strain curve for polyethylene (PE) and a counterpart PE-chitin nanowhisker composite (PE nC);

FIG. 9 is a graph showing a stress/strain curve for acrylonitrile butadiene styrene (ABS) and a counterpart ABS-chitin nanowhisker composite (ABS nC); and

FIG. 10 is a graph showing a stress/strain curve for polycarbonate (PC) and a counterpart PC-chitin nanowhisker composite (PC nC).

DETAILED DESCRIPTION

Turning to FIG. 1, there is shown a flowchart with steps in a method 10 for processing chitin to yield a chitin nanowhisker gel. An initially non-colloidal mixture substantially of chitin and hydrochloric acid is first formed, to subject the chitin to hydrolysis (step 100). In this embodiment, the chitin introduced into the process is in powder form, hydrolysis is conducted between about 80° C. (176° F.) and about 100° C. (212° F.), and the HCl is between about 2.5 N and about 4 N. The hydrolysis may be conducted at higher temperatures, but at lower than the bottom end of this range hydrolysis tends not to be effective.

While both crystalline and amorphous forms of the chitin are chemically the same, they are structurally different enough that the amorphous chitin is more reactive and therefore dissolves faster during acid hydrolysis than does the crystalline chitin. This distinction enables the crystalline form of chitin to withstand dissolution somewhat longer during acid hydrolysis than the amorphous chitin. After a time, which will depend on a number of factors including volumes but may be between about 1 hour and about 4 hours, the mixture will become substantially colloidal with the crystalline chitin dispersed and the amorphous chitin having been dissolved. When the mixture reaches this substantially colloidal state, conditions of the mixture are controlled to rapidly slow or stop the hydrolysis (step 200). This intervention is for limiting the extent to which the crystalline chitin is itself dissolved, so as to preserve crystalline chitin.

In this embodiment, controlling the conditions of the substantially colloidal mixture include both adding an amount of a base such as sodium hydroxide (NaOH) to bring the HCl to below 2.5 N, and applying a chill to the substantially colloidal mixture. Preferably, in order for the process to be carried out safely on an industrial scale, the amount of sodium hydroxide added to the substantially colloidal mixture is less than would be required to cause a violent reaction with the hydrochloric acid. However, lower amounts of sodium hydroxide will limit the rate at which hydrolysis can be slowed or stopped. As such, applying the chill to bring the temperature down rapidly to a temperature at which hydrolysis is significantly slowed or stopped, for example to below 25° C. (77° F.), along with the adding of the base acts in combination to rapidly slow or stop the hydrolysis. Alternatively, just chilling, chilling and diluting with water, or chilling, neutralizing and diluting with water can be done. It will be understood that larger containers will be required if diluting with water, which may be undesirable when implementing the process on an industrial-scale.

With the conditions of the mixture having been controlled to rapidly slow or stop the hydrolysis, the substantially colloidal mixture is then dialysed to produce a processed colloidal mixture consisting substantially of water and crystalline chitin (step 300). The dialysis serves to remove constituents of the mixture other than the water and the crystalline chitin. Advantageously, adding sodium hydroxide to slow or stop hydrolysis in the controlling step also puts the mixture in a condition to increase the rate of dialysis itself, when compared to dialysis with just the hydrochloric acid. In particular, with the addition of sodium hydroxide (NaOH) to the hydrochloric acid (HCl), water and ions of sodium and chlorine (Na⁺ and Cl⁻, respectively), are produced. As such, the osmotic pressure during hydrolysis that is acting individually on each of the Na⁺ and Cl⁻ ions and the residual HCl is, in aggregate, greater than the osmotic pressure that would act independently on individual particles of HCl were the base not added. This increase in the rate of dialysis has the potential to increase the speed at which the process can be executed, which carries advantages when implementing on an industrial scale. In alternative embodiments, with the addition of a different base, different by-products would result. However, the osmotic pressure advantage would remain. Examples of bases include potassium hydroxide, barium hydroxide, cesium hydroxide, sodium hydroxide, strontium hydroxide, calcium hydroxide, lithium hydroxide, and rubidium hydroxide. Other bases may be used, and selection of a base may involve consideration of factors such as the toxicity of the by-products and the ease with which they may be disposed.

In this embodiment, dialysis is conducted using a cellulose semi-permeable membrane having pores that permit egress of HCl, Na⁺ and Cl⁻ without permitting egress of the chitin nanowhiskers in the mixture. As is well known, in order to avoid damaging a cellulose membrane, the temperature of the mixture to be dialyzed should be lower than the about 80° C. to about 100° C. temperature at which the hydrolysis is conducted. As such, chilling during the controlling step serves dual purposes of helping to stop or slow the hydrolysis as well as putting the mixture into a condition for dialysis with the cellulose membrane. The time for dialysis generally depends on the osmotic pressure, so flushing of the opposite side of the membrane may be done on a regular basis based on pH measurements, in an effort to preserve high osmotic pressure over the time dialysis is to be conducted. In an alternative embodiment, osmotic pressure may be increased by applying physical pressure to the mixture to force particles through the membrane. Other semi-permeable membranes may be employed for dialysis that either do not require cooling, or that require more or less cooling than a cellulose semi-permeable membrane.

Pursuant to the dialysis, crystalline chitin will remain that is likely to include agglomerated chitin nanowhiskers as well as individual chitin nanowhiskers. Because large agglomerations of chitin nanowhiskers generally do not impart the beneficial effects for nanocomposites that are imparted by individual chitin nanowhiskers or very small agglomerations of chitin nanowhiskers, it is desirable to separate the individual chitin nanowhiskers and very small agglomerations of chitin nanowhiskers from the large agglomerations of nanowhiskers. As such, following step 300, the amount of agglomerated chitin nanowhiskers in the processed colloidal mixture is reduced, as is the amount of water, in order to yield the chitin nanowhisker gel (step 400).

In this embodiment, during reducing the amount of agglomerated chitin nanowhiskers, the processed colloidal mixture resulting from dialysis is subjected to centrifuging. Since the agglomerated chitin nanowhiskers desired to be removed from the processed colloidal mixture are many times heavier than the individual chitin nanowhiskers that are to remain, the time and speed of centrifuging are controlled to move the agglomerated chitin nanowhiskers out of the main body of the processed colloidal mixture for disposal, without also moving very much individual chitin nanowhiskers. Low RPM is preferred for subjecting the individual chitin nanowhiskers to less force, but there is a trade off with the time it takes to move the agglomerated chitin nanowhiskers from the processing colloidal mixture. Once this centrifuging is conducted, the higher-viscosity layer containing the agglomerated chitin nanowhiskers is separated off and disposed of or routed elsewhere for further processing.

During reducing the amount of water, the processed colloidal mixture with agglomerated chitin nanowhiskers having been removed is subjected to additional centrifuging under different conditions. The goal of this additional centrifuging is to concentrate the chitin nanowhiskers into a high-viscosity layer to produce a chitin nanowhisker gel and to separate off the lower-viscosity layer (substantially water) that contains no or very few chitin nanowhiskers for disposal or routing elsewhere for further processing. In this embodiment, the centrifuging yields a chitin nanowhisker gel that is about 20% chitin nanowhiskers and 80% water, by weight. Control is exercised to ensure the concentration of chitin nanowhiskers in the gel is not too great, because as the concentration of chitin nanowhiskers in the gel rises, the likelihood of agglomeration of the chitin nanowhiskers rises accordingly. As an alternative to, or in combination with, centrifuging, evaporation may be employed for reducing the amount of water.

Preferably the method is conducted on a continuous basis, rather than a batch basis, such that chitin is continuously being input into the process and chitin nanowhisker gel is continuously being yielded by the process. Conducting the method on a continuous basis makes it more amenable to industrial scale production of chitin nanowhisker gel. For example, machines for continuous centrifuging may be employed.

FIG. 2 is an image captured, using an atomic force microscope (AFM) using peak force error mode, of chitin nanowhiskers, wherein the scale bar is included within the image. FIGS. 3 through 5 are images captured, using a transmission electron microscope (TEM), of chitin nanowhiskers.

The chitin nanowhisker gel may be used for producing nanocomposites, or further processed to produce a chitin nanowhisker powder that itself may be used for producing nanocomposites. Preferably, such further processing to produce the chitin nanowhisker powder comprises lyophilising, or freeze-drying, the chitin nanowhisker gel. This is done in order to limit the extent to which the chitin nanowhiskers agglomerate with the loss of water, as compared with simply causing the water in the gel to evaporate. Without wishing to be bound to a particular theory, it is believed that evaporation permits individual chitin nanowhiskers to gradually organize into agglomerations, whereas the nature of freeze-drying limits such opportunities to produce fewer agglomerations.

The chitin nanowhisker gel may be employed in a downstream or separate process for producing nanocomposites having the chitin nanowhiskers dispersed in a bulk solid matrix such as a thermoplastic polymer. Turning to FIG. 6, a method 50 of forming a composite of chitin nanowhiskers dispersed in a thermoplastic polymer matrix is shown. During the method, thermoplastic polymer particles are coated with a chitin nanowhisker gel (step 500) and the coated particles are subjected to melt-blending thereby to form the composite (step 600).

Preferably the particles are pellets having a maximum diameter of about 1 centimetre (cm), and more preferably the majority of the pellets have a diameter of about 2 to about 3 millimetres (mm) The composite may be further processed for form pellets of composite, or further processed to powder form.

Generally, coating is conducted to position nanowhiskers suspended in the gel with respect to the thermoplastic particles so as to facilitate dispersion of the nanowhiskers throughout the melted or softened thermoplastic polymer upon melt-blending. This technique makes it much more likely that a composite will be produced that has more uniform nanowhisker dispersion than those composites produced by methods that merely layer chitin nanowhisker gel atop a layer of the thermoplastic particles just prior to melt-blending. For example, with the prior layering methods, a great number of adjacent thermoplastic particles may not be in contact with, or even physically near to, the nanowhisker gel at the time of melt-blending, and a great volume of nanowhiskers gel may not be in contact with, or even physically near, the thermoplastic particles. In such cases, upon melt-blending sections of thermoplastic matrix can be formed that incorporate too few or too many chitin nanowhiskers, causing uniformity of the nanocomposite to suffer. In particular, sections of the nanocomposite can be formed that do not exhibit the beneficial properties that are desired of the nanocomposite as a whole, despite the correct overall relative amounts of matrix and nanowhiskers.

Furthermore, as the melt-blending involves evaporation of the dispersion medium of the nanowhisker gel, insufficiently coating the particles with nanowhisker gel can result in agglomerations of chitin nanowhiskers rather than dispersion of individual chitin nanowhiskers in the thermoplastic polymer matrix.

Two primary factors determine the viability of the thermoplastic polymer being chosen for the matrix. The first is that, at least where the dispersion medium of the chitin nanowhisker suspension is water, the thermoplastic polymer should have a relatively low melting point at or below about 200 degrees C. The water is useful as a polar liquid medium that keeps the chitin nanowhiskers separated so they can be well-dispersed during melt-blending in the thermoplastic matrix. Accordingly, blending of the chitin nanowhiskers with the thermoplastic polymer during the melt-blending should begin prior to complete evaporation of the water. It will be understood that, where the dispersion medium is not water and has properties that cause it to evaporate differently than a water dispersion medium, a thermoplastic polymer with an accordingly higher melting point may be chosen. Furthermore, the temperature at which melt-blending is done can be regulated to account for various melting temperatures and rates of dispersion medium evaporation, or concentration of water can be established so as to delay full evaporation.

The second factor determining the viability of the thermoplastic polymer being chosen for the matrix relates to water degrading certain thermoplastic polymers during the melt/blending process. For example, if water is the dispersion medium of the suspension, those thermoplastic polymers that are easily degraded by water may not viable. If such water-degradable thermoplastic polymers are to be used, it may be prudent to choose a dispersion medium other than water than will not degrade the thermoplastic polymer. However, it should be borne in mind that, while water can trigger degradation of a given thermoplastic polymer, provided the reinforcement provided by the dispersed chitin nanowhiskers at least makes up for the degradation, the composition formed of that thermoplastic polymer is viable.

While it is preferred that each particle of thermoplastic polymer, whether pellet or powder, be individually coated simply for uniformity of mechanical properties across the entire body of the resultant nanocomposite, as a practical industrial matter not each and every particle must be completely coated in order for the overall body of the composite to benefit from the nanowhiskers.

Furthermore, melt-blending can be conducted under conditions that do not strictly “melt” the thermoplastic polymer, but sufficiently soften the thermoplastic polymer so that the chitin nanowhiskers can be dispersed.

The method of forming a composite described above may be employed to form a composite comprising particles of thermoplastic polymer coated with a chitin nanowhisker gel and melt-blended. The thermoplastic polymer may comprise polypropylene, polyethylene, acrylonitrile butadiene styrene, polycarbonate or other suitable thermoplastic polymer. The composite may comprise about 1% wt. to about 5% wt. chitin nanowhiskers.

EXAMPLES

Composites including chitin nanowhiskers dispersed in various thermoplastic polymers were fabricated. In each case, fabrication generally included coating thermoplastic particles with a chitin nanowhisker gel and subjecting the coated particles to melt-blending thereby forming the composite. In this embodiment, the majority of the particles were pellets with a diameter of about 2-3 millimetres.

In these examples, the dispersion medium of the chitin nanowhisker gel was water, and the chitin nanowhisker gel was produced according to the method described above.

Polypropylene (PP), Polyethylene (PE), Acrylonitrile butadiene styrene (ABS), Polycarbonate (PC) were experimentally determined to be viable for composites along with chitin nanowhisker. For example, viable composites include: a composite comprising chitin nanowhiskers dispersed in polypropylene, a composite comprising chitin nanowhiskers dispersed in polyethylene, a composite comprising chitin nanowhiskers dispersed in acrylonitrile butadiene styrene, and a composite comprising chitin nanowhiskers dispersed in polycarbonate. Various other thermoplastic polymers satisfying the above two conditions are likely to be viable candidates. In one embodiment, melt-blending was conducted 15-20 degrees above the melting temperature of the thermoplastic polymer to be used. At 20% chitin concentration, the gel was 5-10% wt. of the thermoplastic polymer pellets.

Compositions comprising about 1% wt. chitin nanowhiskers compositions were fabricated as described above, and the fabricated compositions were subjected to tensile testing. In particular, tensile testing involved characterizing the tensile properties of the composites and foams on a tensile testing system (Instron Micro Tester 5848). The composition specimens were fabricated in accordance with ASTM D638 type 5 standard dogbone shape (7.62 mm gage length, 3 mm width, 1.5 mm thickness) and tensile tested with a strain rate of 0.5 mm/minute.

FIGS. 7 through 10 are graphs showing typical stress/strain curves, for respective ones of the above-described tests of PP, PE, ABS and PC alone and the respective 1% nanocomposite counterparts. All graphs represent test results as the average of four (4) samples. Typical stress/strain curves are presented.

Table 1 below summarizes the comparisons of Ultimate Tensile Strength (UTS), Modulus, and Elongation between PP and the corresponding nanocomposite (PP nC) as depicted in the graph of FIG. 7:

TABLE 1 PP PP nC UTS 31.57 ± 0.61 34.17 ± 0.786 Modulus 363.29 ± 24.96 433.35 ± 34.23  Elongation   0.203 ± 0.015275  0.1707 ± 0.02269

Table 2 below summarizes the comparisons of Ultimate Tensile Strength (UTS), Modulus, and Elongation between PE and the corresponding nanocomposite (PE nC) as depicted in the graph of FIG. 8:

TABLE 2 PE PE nC UTS 18.39 ± 0.955 20.31 ± 0.831 Modulus 248.17 ± 19.437 258.44 ± 16.474 Elongation 0.358 ± 0.054  3.03 ± 0.975

Table 3 below summarizes the comparisons of Ultimate Tensile Strength (UTS), Modulus, and Elongation between ABS and the corresponding nanocomposite (ABS nC) as depicted in the graph of FIG. 9:

TABLE 3 ABS ABS nC UTS 17.81 ± 0.938 19.42 ± 0.366 Modulus 428.09 ± 16.02  440.61 ± 4.57  Elongation  0.45 ± 0.255  0.585 ± 0.0517

Table 4 below summarizes the comparisons of Ultimate Tensile Strength (UTS), Modulus, and Elongation between PC and the corresponding nanocomposite (PC nC) as depicted in the graph of FIG. 10:

TABLE 4 PC PC nC UTS  57.06 ± 0.5416  59.12 ± 0.4588 Modulus 442.53 ± 14.79 494.85 ± 15.66  Elongation 0.4475 ± 0.166 0.3279 ± 0.0168

Although embodiments have been described with reference to the drawings, those of skill in the art will appreciate that variations and modifications may be made without departing from the spirit and scope thereof as defined by the appended claims. 

What is claimed is:
 1. A composite comprising particles of thermoplastic polymer coated with a chitin nanowhisker gel and melt-blended.
 2. The composite of claim 1, wherein the chitin nanowhisker gel is 5-10% wt. of the thermoplastic polymer.
 3. The composite of claim 1, wherein the chitin nanowhiskers are about 20% wt. of the gel suspension.
 4. The composite of claim 1, wherein the thermoplastic polymer comprises polypropylene.
 5. The composite of claim 1, wherein the thermoplastic polymer comprises polyethylene.
 6. The composite of claim 1, wherein the thermoplastic polymer comprises acrylonitrile butadiene styrene.
 7. The composite of claim 1, wherein the thermoplastic polymer comprises polycarbonate.
 8. The composite of claim 1, wherein the composite is comprised of about 1% wt. to about 5% wt. chitin nanowhiskers.
 9. The composite of claim 1, wherein the composite is comprised of about 1% wt. chitin nanowhiskers.
 10. A composite comprising chitin nanowhiskers dispersed in polypropylene.
 11. The composite of claim 10, wherein powder chitin nanowhiskers are melt-blended with the polypropylene.
 12. The composite of claim 10, wherein a gel suspension of the chitin nanowhiskers is melt-blended with the polypropylene.
 13. The composite of claim 12, wherein the polypropylene is coated with the gel suspension and melt-blended.
 14. A composite comprising chitin nanowhiskers dispersed in polyethylene.
 15. The composite of claim 14, wherein powder chitin nanowhiskers are melt-blended with the polyethylene.
 16. The composite of claim 14, wherein a gel suspension of the chitin nanowhiskers is melt-blended with the polyethylene.
 17. The composite of claim 16, wherein the polyethylene is coated with the gel suspension and melt-blended.
 18. A composite comprising chitin nanowhiskers dispersed in acrylonitrile butadiene styrene.
 19. The composite of claim 18, wherein powder chitin nanowhiskers are melt-blended with the acrylonitrile butadiene styrene.
 20. The composite of claim 19, wherein a gel suspension of the chitin nanowhiskers is melt-blended with the acrylonitrile butadiene styrene.
 21. The composite of claim 20, wherein the acrylonitrile butadiene styrene is coated with the gel suspension and melt-blended.
 22. A composite comprising chitin nanowhiskers dispersed in polycarbonate.
 23. The composite of claim 22, wherein powder chitin nanowhiskers are melt-blended with the polycarbonate.
 24. The composite of claim 22, wherein a gel suspension of the chitin nanowhiskers is melt-blended with the polycarbonate.
 25. The composite of claim 24, wherein the polycarbonate is coated with the gel suspension and melt-blended. 